Glass fiber cord with a hook weave ESS/HC Type
Technical specification – description
The cord ESS/HC type is manufactured from textured yarn made of boro-alumino-silicate E type glass of temperature resistance up to 650°C. Thanks to application of a knitting method of weaving, significant softness and flexibility of sealing have been achieved, which to a large extent facilitates fitting in fireplace inserts. A standard finished product is supplied on cardboard spools in sections of 100 running meters long.
Technical parameters:
| PARAMETER DESCRIPTION | VALUE |
| Type | ESS/HC |
| Raw material | Textured glass yarn type E Ø 9 µm |
| Method of execution | Hooked, without core |
| Maximum temperature of short-term use | 650º C |
| Maximum temperature of continuous use | 500º C |
| Minimum temperature of use | -100º C |
| pH range | 3 - 14 |
| Reinforcement type | none |
| Density | 0,6 g / cm3 |
| Color | Black or dark grey |
| Dimension range | Ø 5 – 14 mm |
Glass fiber tapes
Technical specification – description
The glass fiber tape is manufactured from textured yarn made of boro-alumino-silicate E type glass of temperature resistance up to 650°C. Thanks to application of a knitting method of weaving, significant softness and flexibility of sealing have been achieved, which to a large extent facilitates fitting in fireplace inserts. A standard finished product is supplied on cardboard spools in sections of 100 running meters long.
| PARAMETER DESCRIPTION | VALUE |
| Type | Free, without core |
| Raw material | Glass yarn |
| Weave | Plain, single-layer or multi-layer (depending on thickness) |
| Maximum temperature of short-term use | 650º C |
| Maximum temperature of continuous use | 500º C |
| Minimum temperature of use | -100º C |
| Melting point of fibers | 1000º C |
| Contractility in % (24 h in 800° C) | Max. 3% |
| Density | 1-1,1 g / cm3 |
| Color | Black or dark grey |
| Dimension range | Width: 10 – 100 mm Thickness: 2 – 20 mm |